Soluble Magnesium Alloy with High Strength for Oil Extraction Industry

• Die Casting Machine Type: Hot Chamber Die Casting Machine
• Die Casting Method: Soluble Die Casting
• Application: Oil Extraction Industry
• Machining: CNC Machining
• Material: Magnesium Alloy/Aluminum Alloy
• Surface Preparation: Customized
• Model NO.: AZ31B, ZK61M, WE43
• Pressure Chamber Structure: 1
• Tolerance Grade: 4
• Casting Surface Quality Level: 1
• Certification: ISO 9001:2000, ISO 9001:2008
• Transport Package: Wood Box
• Specification: customized
• Trademark: galliumwafers
• Origin: China
• HS Code: 8104190000
• Production Capacity: 1000mt/Year

Product Description

 

Type	Magnesium alloy rod
Size	Diameter 90-110-120mmx1000mm,or as customer's required
Application	0il extraction industry
Features	1.Good resistance to deformation force
	2.Good sag resistance
	3.Good absorption of vibration energy performance
	4.Good impact energy absorption characteristics
	5.Low melting, small specific heat
Surface	Ordinary industrial surface,or customized
Material	Magnesium alloy

We can supply Soluble Magnesium Alloy with density:1.5-2.0 g/cm^{3,suplier light} Mg-Li series,high strength heat resisting Mg-RE series,Mg-Al series,Mg-Zn series, high strenght can reach above 400Mpa.

No						Dissolve the environment	Dissolution rate/(mg/cm2h)
	Density  (g/cm-3)	Tensile strength/MPa	Yield strength/MPa	Elongation/%	Hardness/HV
QYM-1	1.99	340-355	245-265	8-15	70-85	90ºC,3%	195~225
QYM-2	1.93	290-330	220-250	10-14	65-72	90ºC,3%	185~200
QYM-3	2.02	330-350	250-280	6-10	70-80	90ºC,3%	335~350
QYM-4	1.84	180-220	130-150	15-20	40-50	90ºC,3%	235~250
QYM-5(T5)	1.41	100-120	85-105	30-50	35-45	50ºC,0.84%	55~70
QYM-5-1(T5)	1.43	110-120	90-110	35-55	35-45	50ºC,0.84%	10~25
QYM-6	1.86	280-300	180-200	15-20	50-60	90ºC,3%	60~75

Can also supply Soluable aluminum alloy with density 2.5-2.8g/cm³,Strength more than 500MPa

No						Dissolve the enviroment	Dissolution rate/(mg/cm2h)
	Density (g/cm-3)	Tensile strength/MPa	Yield strength/MPa	Elongation/%	Hardness /HV
QY-3(T6)	2.80	530-560	450-480	5-8	140-155	60ºC,3%	3~10
QY-6	2.65	260-290	120-140	15-20	75-85	60ºC,3%	10~30