Copper Beryllium Alloy Cube2 Cube4 Cube10 Used for Smelting

• Product Type: Lump/Ball/Wire/Strip/Ingot
• Material: Cube2/Cube4/Cube10
• Carbon Content: Low Carbon
• PCD: 100mm
• ET: 15mm
• Hole: 5
• Model NO.: Cube2/CuBe3.8/CuBe4 / CuBe10
• Color: Gold
• Shape: Lump\Ingot
• MOQ: 5-7kg
• Product: Cube2,Cube3.8,Cub4,Cube10
• Transport Package: Wood Pallets or Box
• Specification: lump/ball/wire/strip/ingot
• Trademark: CHALCO, ZSXC
• Origin: China
• HS Code: 740500
• Production Capacity: 1000mt/Year

Product Description

Beryllium copper alloy CuBe2 CuBe4 CuBe10 with Be 2-10% used for melting 

Beside CuBe2 CuBe4 CuBe10,we can also suppy below aluminum master alloy :Albe3/AlBe5/Alsc2/Alti5b/Alni10/Alti10/Alsi20/AlCu50/AlZr/ALcR/AlCr/AlV etc.

Name	Brand	Alloy elements %	Use	Add the amount	Melt temperature ºC	Features
Copper silicon	CuSi16	Si13.5~16.5	Adjust ingredients to improve plasticity	Needs vary	800	crispy
Copper and manganese	CuMn22	Mn20~25	Fine grain, improve plasticity and eliminate hot - rolled crack	2~3‰	850~900	toughening
Copper and nickel	CuNi15	Ni14~18	Adjust ingredients to improve plasticity	2~3‰	1050~1200	toughening
Copper and iron	CuFe10	Fe9~11	Refine the grain and improve the plasticity of cold working	3~5‰	1300~1400	toughening
Copper  antimony	CuSb50	Sb49~51	Fine grains	2~3‰	680	crispy
Beryllium copper	CuBe4	Be3.8~4.8	Fine grains	1~3‰	1100~1200	toughening
Copper phosphorus	CuP14	P13~15	Grain refining, degassing deoxygenation	1~3‰	900~1020	crispy
Copper  magnesium	CuMg10	Mg9~11	Fine grains	1~3‰	750~800	crispy
Copper rare earth	CuRe15	Re14~16	Grain refining, desulphurization, deoxidation, improve performance, improve electrical conductivity	2~4‰	1050~1200	toughening
Copper  titanium	CuTi20	Ti18~20	Fine grains	1~5‰	970~1020	toughening
Copper and zirconium	CuZr10	Zr8~12	Fine grains	2~3‰	1100~1200	toughening
Copper boron	CuB3	B3~3.8	Improve electrical conductivity	0.5~2‰	1200~1250	toughening
The chemical composition impurities of copper intermediate alloy are produced according to YS/283-1994 standard