Suspension PVDF Resin Material Extrusion Grade Copolymer
| US$1.00 | 1 Piece (MOQ) |
Port:
Tianjin, China
Production Capacity:
10000mt/Year
Payment Terms:
L/C, T/T, Western Union, Paypal, Money Gram, bank transfer
Zhengzhou Alloy New Reserves Co., Ltd.
Henan, China
Last Login Date:
Jul 21, 2025
Business Type:
Manufacturer/Factory, Trading Company
Main Products:
Aluminum Alloy, Magnesium Rare Earth Alloy Sheet Plate Bar Wire, Magnesium Lithium Alloy Sheet Plate Foil, Aluminum Lithium Alloy Sheet Plate, Copper Alloy, Zinc Alloy, Indium/Germanium Metal/Oxide, GaAs/Sillicon/Sic/Germanium/GaN/Gap Wafer, Dry Mortar Machine
Product Description
Company Info
Basic Info.
Model NO.
PVDF
CAS No.
24937-79-9
Formula
(C2h2f2)N
EINECS
677-810-1
Material
Copolymer PVDF
Usage
General Plastics, Injection Grade,Lithium Battery Binder,Extrusion
Plastic Properties After Heated
Thermoplastic Plastics
Plastic Forming Method
Both
Color
White
Trademark
galliumwafers
Transport Package
Transport by Car or Other
Specification
granule, powder
Origin
China
HS Code
39046900
Product Description
| General | ||
| Features | Copolymer, Medium and low viscosity | |
| Uses | Extruded pipe, Bar, Plate | |
| Forms | Translucent white particles | |
| Items | Typical Value FL2606 | Test Method |
| Physical Properties | ||
| Density(g/cc) | 1.77~1.80 | ASTM D792 |
| Melt Flow Rate(g/10min) | 4.0~8.0 | Load 5kg, 230ºC,ASTM D1238 |
| Melt viscosity(Kps) | 10~15 | Shear Rate 100 1/s, ASTM D3835 |
| Water Absorption(%)(Time 24 hr) | ≤0.040 | ISO 62 |
| Linear Mold Shrinkage(cm/cm) | 0.0200~0.0300 | |
| Molecular Properties | ||
| Molecular weight(Da) | 350,000~440,000 | GPC,DMF,ISO 16014 |
| Intrinsic viscosity(dl/g) | 1.10~1.30 | 30ºC,DMAC |
| Molecular weight distribution | 2.0-3.0 | GPC,DMF,ISO 16014 |
| Mechanical Properties | ||
| Tensile Modulus(Thickness2.00mm)(MPa) | 800~1200 | 1.0mm/min,ASTM D638 |
| Flexural Modulus(Thickness2.00mm)(MPa) | 700~1000 | 2.0mm/min,ASTM D790 |
| Yield Strength(Thickness2.00mm)(MPa) | 30.0~40.0 | 50mm/min,ASTM D638 |
| Break Strength(Thickness2.00mm)(MPa) | 20.0~35.0 | 50mm/min,ASTM D638 |
| Elongation at Yield(%) | 10.0~15 | 50mm/min,ASTM D638 |
| Elongation at Break(%) | 200~600 | 50mm/min,ASTM D638 |
| Hardness, Shore D(Thickness2.00mm) | 70~75 | ASTM D2240 |
| Izod Impact, Notched(Thickness 4.00mm, 23ºC)(J/m) | 150~200 | Notched V 10 mm ASTM D256 |
| Thermal Properties | ||
| Melting Point(ºC) | 158~166 | ASTM D3418 |
| Crystallization Temperature(DSC peak)(ºC) | 115~130 | ASTM D3418 |
| Glass Transition Temp, Tg(ºC) | -32.0 | ASTM E1356 |
| Decomposition Temperature(ºC) | 330~350 | 1% wt. loss / in air |
| Vicat Softening Point(ºC) | 90~105 | ASTM D1525 |
| Heat deflection temperature at 1.8 MPa(Thickness 4.00mm)(ºC) | 50~60 | After annealing 150ºC,16h ASTM D648 |
| Electrical Properties | ||
| Surface Resistance(ohm) | ≥1.00E+14 | Voltage<1V,After 2 min-500V ASTM D257 |
| Electrical Resistivity(ohm·cm) | ≥1.00E+14 | Intensity=10mA,After 2 min@23ºC ASTM D257 |
| Dielectric strength(Thickness 1.00mm,23ºC)(KV/mm) | 20~25 | ASTM D149 |
| Dielectric constant(1kHz,23ºC) | 7.0~10.0 | ASTM D150 |
| Burning Properties | ||
| UL Flame retardant grade(0.100mm) | V-0 | UL94 |
| Oxygen Index(3.00mm) | 44% | ASTM D2683 |
This product should be processed under 260ºC to avoid producing toxic gases.
PVDF has good fire resistance and smoke inhibition property. While, it will release toxic xxxx gas and fluorocarbon compounds when meets with fire.
Operators should pay attention to personal protection during the processing and operating.
Packaging and storage
PVDF is packed in a plastic bag and then be put into a PE bag with the net weight 25KGS. It must be stored in clean, cool, dry place.
Send your message to this supplier
People who liked this also liked
US$29.50-32.00
5 kg (MOQ)
US$7.00-8.20
25 kg (MOQ)
US$19.00-25.00
1 kg (MOQ)
US$29.50-32.00
5 kg (MOQ)
US$29.50-32.00
5 kg (MOQ)
US$19.50-22.30
1 kg (MOQ)
US$19.00-25.00
1 kg (MOQ)
US$17.20-19.90
1 kg (MOQ)
US$28.00-36.00
10 Kg (MOQ)